A new form of dual-phase heterostructured nanosheet comprised of oxygen-deficient TiO2/Li4Ti5O12 has been successfully synthesized and used as anode material for lithium ion batteries. With the three-dimensional (3D) Ti mesh as both the conducting substrate and the Ti(3+)/Ti(4+) source, blue anatase Ti(3+)/TiO2nanosheets were grown by a hydrothermal reaction. By controlling the chemical lithiation period of TiO2 nanosheets, a phase boundary was created between the TiO2 and the newly formed Li4Ti5O12, which contribute additional capacity benefiting from favorable charge separation between the two phase interfaces. Through further hydrogenation of the 3D TiO2/Li4Ti5O12 heterostructured nanosheets (denoted as H-TiO2/LTO HNS), an extraordinary rate performance with capacity of 174 mAh g(-1) at 200 C and outstanding long-term cycling stability with only an ∼6% decrease of its initial specific capacity after 6000 cycles were delivered. The heterostructured nanosheet morphology provides a short length of lithium diffusion and high electrode/electrolyte contact area, which could also explain the remarkable lithium storage performance. In addition, the full battery assembled based on the H-TiO2/LTO anode achieves high energy and power densities.
Keywords: TiO2−Li4Ti5O12; heterostructured nanosheet; lithium ion battery; oxygen vacancy; phase boundary.