Charge Compensating Defects in Methylammonium Lead Iodide Perovskite Suppressed by Formamidinium Inclusion

Niraj Shrestha; Zhaoning Song; Cong Chen; Ebin Bastola; Xiaoming Wang; Yanfa Yan; Randy J Ellingson

doi:10.1021/acs.jpclett.9b03234

Charge Compensating Defects in Methylammonium Lead Iodide Perovskite Suppressed by Formamidinium Inclusion

J Phys Chem Lett. 2020 Jan 2;11(1):121-128. doi: 10.1021/acs.jpclett.9b03234. Epub 2019 Dec 16.

Authors

Niraj Shrestha¹, Zhaoning Song¹, Cong Chen¹, Ebin Bastola¹, Xiaoming Wang¹, Yanfa Yan¹, Randy J Ellingson¹

Affiliation

¹ Department of Physics and Astronomy, Wright Center for Photovoltaics Innovation and Commercialization , University of Toledo , Toledo , Ohio 43606 , United States.

PMID: 31820989
DOI: 10.1021/acs.jpclett.9b03234

Abstract

Temperature-dependent photoluminescence (PL) spectroscopy measurements have been performed over a range from 9 K to room temperature on polycrystalline methylammonium (MA)/formamidinium (FA) lead iodide (MA_1-xFA_xPbI₃) perovskite thin films. Our low-temperature PL analysis reveals the existence of charge compensating defects in MAPbI₃, which may explain the lower net free carrier concentration in MAPbI₃ perovskite. More interestingly, we observe the suppression of the PL emission associated with the charged defects by appropriate FA inclusion. Furthermore, FA incorporation into MAPbI₃ has been found to slow the phase transformation of MA_1-xFA_xPbI₃ from orthorhombic to tetragonal phase, which occurs with increasing temperature. Our analyses of the FA concentration's impact on defect density and structural phase transformation provide beneficial insights that improve the understanding of the photovoltaic properties and application of organic-inorganic metal halide perovskites.