The efficiencies of small-pixel perovskite photovoltaics have increased to above 24%, while most reported fabrication methods cannot be transferred to scalable manufacturing process. Here, we report a method of fast blading large-area perovskite films at an unprecedented speed of 99 mm/s under ambient conditions by tailoring solvent coordination capability. Combing volatile noncoordinating solvents to Pb2+ and low-volatile, coordinating solvents achieves both fast drying and large perovskite grains at room temperature. The reproducible fabrication yields a certified module efficiency of 16.4%, with an aperture area of 63.7 cm2. This method can be applied for various perovskite compositions. The perovskite modules also show a small temperature coefficient of -0.13%/°C and nearly fully recoverable efficiency after 58 cycles of shading, much better than commercial silicon and thin-film solar modules.
Copyright © 2019 The Authors, some rights reserved; exclusive licensee American Association for the Advancement of Science. No claim to original U.S. Government Works. Distributed under a Creative Commons Attribution NonCommercial License 4.0 (CC BY-NC).