The development of high-performance rubber composites has always been a research hotspot in the field of conveyor belt manufacturing. In this work, a rubber cover joint composite made of reduced graphene oxide (rGO) was prepared using latex mixing and mechanical blending methods, with a steel wire rope conveyor belt as the research object, and the influence of the rGO content on the properties of the rubber composite is discussed. The structure and morphology characterization of the rGO/NR rubber show that the addition of rGO does not change its crystal structure, and 1.2 phr rGO is uniformly dispersed throughout the rubber composite. As more rGO is added, the mechanical properties of the rGO rubber cover joint first improve and then worsen. With the addition of 1.2 phr, the cross-linking density increases by 80.6%, the tensile strength of the rubber composites increases by 49.7%, the elongation at break increases by 23.6%, and the adhesion strength increases by 12.4%. The tensile strength of the rGO rubber cover joint can still maintain 72.5% of its pre-thermal aging value. The wear resistance and thermal conductivity increase as more phr is added. When 3.0 phr is added, the wear resistance of the rubber composites increases by 32.9%, the thermal conductivity increases by 118.8%, and the temperature difference at the completion of vulcanization decreases from 4.5 °C to 1.8 °C. The results show that when 1.2 phr of rGO is added, the rubber conveyor belt joint obtains the best comprehensive performance. These enhanced comprehensive properties allow for the practical application of rGO nanomaterials to conveyor belt rubber.
Keywords: conveyor belt; mechanical properties; reduced graphene oxide; rubber cover joint.