Infrared (IR) solar cells, capable of converting low-energy IR photons to electron-hole pairs, are promising optoelectronic devices by broadening the utilization range of the solar spectrum to the short-wavelength IR region. The emerging PbS colloidal quantum dot (QD) IR solar cells attract much attention due to their tunable band gaps in the IR region, potential multiple exciton generation, and facile solution processing. In PbS QD solar cells, ZnO is commonly utilized as an electron transport layer (ETL) to establish a depleted heterostructure with a QD photoactive layer. However, band gap shrinkage of large PbS QDs makes it necessary to tailor the behaviors of the ZnO ETL for efficient carrier extraction in the devices. Herein, the characteristics of ZnO ETL are efficiently and flexibly tailored to match the QD layer by handily adjusting the postannealing process of ZnO ETL. With a suitable temperature, the well-matched energy level alignment and suppressed trap states are simultaneously achieved in the ZnO ETL, effectively reducing the nonradiative recombination and accelerating the electron injection from the QD layer to ETL. As a consequence, a high-performance PbS QD photovoltaic device with power conversion efficiencies (PCEs) of 10.09% and 1.37% is obtained under AM 1.5 and 1100 nm filtered solar illumination, demonstrating a simple and effective approach for achieving high-performance IR photoelectric devices.
Keywords: PbS quantum dots; ZnO film; electron transport layer; infrared solar cells; post-treatment process.