As a result of full-scale ongoing global efforts, the power conversion efficiency (PCE) of the organic-inorganic metal halide perovskite has skyrocketed. Unfortunately, the long-term operational stability for commercialization standards is still lagging owing to intrinsic defects such as ion migration-induced degradation, undercoordinated Pb2+, and shallow defects initiated by disordered crystal growth. Herein, we employed multifunctional, non-volatile tetra-methyl guanidine hydrochloride [TMGHCL] ionic liquid (IL) as an additive to elucidate defects' passivation effects on organic-inorganic metal halide perovskite. More specifically, the formation of hydrogen bonds between H+ in GA+ and I- and coordinate bonding between Cl- and undercoordinated PbI2+could significantly passivate these defects. The hypothesis was confirmed by both experimental and DFT simulations displaying that the optimized ratio of IL integration restrains ion migration, improving grains' size, and significantly elongating the carrier lifetime. Remarkably, the modified cell achieved a peak efficiency of 22.00% with negligible hysteresis, compared to the control device's PCE of 20.12%. In addition, the TMGHCL-based device retains its 93.29% efficiency after 16 days of continuous exposure to air. This efficient approach of adding IL to perovskites absorber can produce high PCE and has strong commercialization potential.
Keywords: Enhanced Performance; Guanidium Ionic Liquid; Interreactions; Long-term Stability; Perovskites Solar Cells.
© 2024 Wiley‐VCH GmbH.