A thermal reaction of Li3N and GaCl3 in which benzene was used as the solvent under pressure has been carried out for the preparation of 30-nanometer particles of gallium nitride (GaN) at 280°C. This temperature is much lower than that of traditional methods, and the yield of GaN reached 80%. The x-ray powder diffraction pattern indicated that sample was mainly hexagonal-phase GaN with a small fraction of rocksalt-phase GaN, which has a lattice constant a = 4.100 angstroms. This rocksalt structure, which had been observed previously only under high pressure (at least 37 gigapascals) was observed directly with high-resolution electron microscopy.