A modulated structure has been fabricated from high transition temperature superconductors where the individual CuO(2) planes are composed of alternating superconducting and insulating strips. This structure is made by growing a-axis-oriented YBa(2)Cu(3)O(7)/PrBa(2)Cu(3)O(7) superlattices by 90 degrees off-axis sputtering on (100)SrTiO(3) and (100)LaAlO(3) substrates. Superlattice modulation is observed to a modulation wavelength of 24 angstroms (12 angstroms-YBa(2)Cu(3)O(7)/12 angstroms-PrBa(2)Cu(3)O(7)), both by x-ray diffraction and by cross-sectional transmission electron microscopy. Rutherford backscattering spectroscopy indicates a high degree of crystalline perfection with a channeling minimum yield of 3 percent. Quasi-one-dimensional conductivity should be obtainable in these structures.