Polypropylene (PP) mesh is the most widely used prosthetic material in hernia repair. However, the efficacy of implanted PP mesh is often compromised by adhesion between viscera and PP mesh. Thus, there is a recognized need for developing an anti-adhesive PP mesh. Here, a composite hydrogel coated PP mesh with the prevention of adhesion after hernia repair was designed. The composite hydrogel coating was prepared from polyvinyl alcohol (PVA) and hyaluronic acid (HA) by using the freezing-thawing (FT) method. To overcome the shortcoming of the long time of the traditional freezing-thawing method, a small molecule 3,4-dihydroxyphenylacetic acid (DHPA) was introduced to promote the formation of composite hydrogel. The as-prepared composite hydrogel coating displayed modulus more closely resembling that of native abdominal wall tissue. In vitro studies illustrated that the resulting meshes showed excellent coating stability, hemocompatibility, and non-cytotoxicity. In vivo experiments using a rat abdominal wall defect model demonstrated that the composite hydrogel coated PP mesh could prevent the formation of adhesion, alleviate the inflammatory response, and reduce the deposition of collagen around the damaged tissue. These disclosed results manifested that the PP mesh coated with HA/PVA composite hydrogel might be a promising application in preventing adhesion for hernia repair.
Keywords: Anti-adhesive polypropylene mesh; Hyaluronic acid; Polyvinyl alcohol.
Copyright © 2024 Elsevier B.V. All rights reserved.