Polypropylene (PP) is a commodity material that has been increasingly used in different industries in the past two decades due to its versatile properties when enhanced with additives. Homo polypropylene, in general, has weak mechanical properties and limited chemical resistance; thus, using a different type of fillers to adjust such properties to fit the required applications opened a large market for this commodity. Understanding the interface constituent between the polymer matrix and the added filler and the nucleation behavior is a key to fine control of the enhancement of PP properties. In this study, PP was incorporated with nano calcium carbonate (CaCO3) at 2 and 5 wt% in the presence of maleic anhydride (MAH) to overcome the weak interface due to low polymer polarity. The mix was compounded in a twin screws extruder at a temperature range of 180-200 °C ; then, the prepared samples were left to dry for 24 h at 25 °C. Nuclear Magnetic Resonance (NMR) was used to study the interface adhesion of the nanofiller and the curved revealed that at 2% of nano CaCO3 PP structure remained the same and the nano experienced good adhesion to the polymer matrix. The mechanical impact resistance results showed a real enhancement to the polymer matrix of the nanocomposite by 37%. Moreover, DSC results showed a faster crystallinity rate due to the nanofiller acting as a nucleating agent and rheology tests indicated that low content of nano additive (2%) has better processability behavior, with suitable viscosity complex values at high frequencies.
Keywords: NMR; interface; nano CaCO3; nanocomposite; nucleation; polypropylene; thermomechanical.