Anion solvation in electrolytes can largely change the electrochemical performance of the electrolytes, yet has been rarely investigated. Herein, three anions of bis(trifluoromethanesulfonyl)imide (TFSI), bis(fluorosulfonyl)imide (FSI), and derived asymmetric (fluorosulfonyl)(trifluoro-methanesulfonyl)imide (FTFSI) are systematically examined in a weakly Li+ cation solvating solvent of bis(3-fluoropropyl)ether (BFPE). In-situ liquid secondary ion mass spectrometry demonstrates that FTFSI- and FSI- anions are associated with BFPE solvent, while weak TFSI- /BFPE cluster signals are detected. Molecular modeling further reveals that the anion-solvent interaction is accompanied by the formation of H-bonding-like interactions. Anion solvation enhances the Li+ cation transfer number and reduces the organic component in solid electrolyte interphase, which enhances the Li plating/stripping Coulombic efficiency at a low temperature of -30 °C from 42.4% in TFSI-based electrolytes to 98.7% in 1.5 m LiFTFSI and 97.9% in LiFSI-BFPE electrolytes. The anion-solvent interactions, especially asymmetric anion solvation also accelerate the Li+ desolvation kinetics. The 1.5 m LiFTFSI-BFPE electrolyte with strong anion-solvent interaction enables LiNi0.8 Mn0.1 Co0.1 O2 (NMC811)||Li (20 µm) full cell with stable cyclability even under -40 °C, retaining over 92% of initial capacity (115 mAh g-1 , after 100 cycles). The anion-solvent interactions insights allow to rational design the electrolyte for lithium metal batteries and beyond to achieve high performance.
Keywords: Anion solvation; Li metal batteries; asymmetric; electrolyte design; low temperature.
© 2023 Wiley-VCH GmbH.