Aim: In-vitro evaluation of shear bond strength, mode of failure, and adaptation of fifth-generation (etch-and-rinse), seventh-generation,and eighth-generation self-etch dental adhesives to human dentin with or without diode-laser irradiation before photopolymerization.
Materials and methods: Seventy-two extracted human maxillary premolar teeth were collected. The buccal and lingual surfaces of teeth were grounded until dentin was exposed. Test areas of 4 mm diameter were created on both surfaces of teeth to standardize the area of treatment. The samples were then randomly allocated into three groups (n = 24): Group 1 Adper Single Bond 2 Etch-and-Rinse; Group 2 Tetric-N-Bond Universal Self-Etch; Group 3 Prime and Bond Universal Self-Etch dental adhesives were used. Buccal surfaces (sub-groups 'a') of all specimens were irradiated with diode laser before photopolymerization of the adhesive material, and palatal surfaces (sub-groups 'b') were directly photopolymerized without prior diode laser irradiation and restored with composite resin. All specimens were thermocycled. Four specimens from each group were then subjected to scanning electron microscopy (SEM) analysis to examine the adaptation of adhesive to dentin, and the remaining 60 specimens were evaluated for shear bond strength tests, modes of failure at the adhesive-dentin interface, and values were recorded, tabulated, and used for data analysis. A one-way ANOVA test and the Student's t-test were used for statistical analysis. A P value ≤ 0.05 was considered statistically significant.
Results: The mean shear bond strength for the groups was: Group 1a (13.96 MPa), 1b (14.95 MPa); Group 2a (10.06 MPa), 2b (10.30 MPa); Group 3a (12.03 MPa), and 3b (10.44 MPa). No statistically significant difference was seen among sub-groups 1a and 3a, 2a and 3a, 2b and 3b as P > 0.05. A significant difference was seen among sub-groups 1b and 3b (P<0.05), 1a and 2a, and 1b and 2b (P<0.01).
Conclusion: Adper Single Bond 2 without diode-laser irradiation before photopolymerization showed the highest shear bond strength, followed by Adper Single Bond 2 irradiated with diode laser before photopolymerization, with the maximum adaptation of dental adhesive to dentin compared to other adhesives used either with or without diode-laser irradiation.
Keywords: adhesive-dentin interface; dentistry; diode-laser; irradiation; photopolymerization; shear bond strength.