We have investigated pressure-induced amorphization (PIA) of an alcohol clathrate hydrate (CH) of cubic structure type I (sI) in the presence of NH4F utilizing dilatometry and x-ray powder diffraction. PIA occurs at 0.98 GPa at 77 K, which is at a much lower pressure than for other CHs of the same structure type. The amorphized CH also shows remarkable resistance against crystallization upon decompression. While amorphized sI CHs could not be recovered previously at all, this is possible in the present case. By contrast to other CHs, the recovery of the amorphized CHs to ambient pressure does not even require a high-pressure annealing step, where recovery without any loss of amorphicity is possible at 120 K and below. Furthermore, PIA is accessible upon compression at unusually high temperatures of up to 140 K, where it reaches the highest degree of amorphicity. Molecular dynamics simulations confirm that polar alcoholic guests, as opposed to non-polar guests, induce cage deformation at lower pressure. The substitution of NH4F into the host-lattice stabilizes the collapsed state more than the crystalline state, thereby enhancing the collapse kinetics and lowering the pressure of collapse.
© 2024 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license (https://creativecommons.org/licenses/by/4.0/).